Parameter	Specification
Name	Control Horizontal Anodizing Line
Output	750 tons per month
Model Type	Horizontal U mode
Operation	Semiautomatic or Automatic
Racking method	Manual racking system

Design Conditions

Alloy: Aluminium 6061 to 6063 or others
Anodizing film thickness: 10~12µm micron
Average coverage area: 350m²/T (ton)
Max aluminium profile length: 6500mm
Extrusion ratio: 2.5kg/m²
Working hours: 300d/m × 20h/d = 600h/m
Racking system: Two fixtures per rack
Racking operation: Manual
Equipment Usage Rate: 0.9
Power supply: AC 3phase 380V 50Hz
Control Power: AC220V 50Hz
Water supply: 2kg/cm²*G
Hot steam: 6kg/cm²*G
Compressor air: 6kg/cm²*G

Process Tank Configuration

Degreasing (Free sulfuric acid 180±30 g/l) - 1 Tank
Alkaline Etching (Free alkali 40-60g/l, Al³⁺ 30-120g/l) - 2 Tanks
Neutralization (Free sulfuric acid 180±20g/l) - 1 Tank
Anodising (Free sulfuric acid 140-180g/l, Al³⁺≤20g/l) - 3 Tanks
Colouring (Stannous sulfate 3-8g/l, Free sulfuric acid 15-25g/l, PH 0.8-1.2) - 1 Tank
Medium Temperature Sealing (PH 5-6.5, Nickel ion 0.8-1.3g/l, Fluorion 0.3-0.7 g/l) - 1 Tank

Treatment Process Details

Degreasing

6 jigs (racks) per tank × 1 tank = 6 jigs
Treatment time: 2-5 minutes

Alkaline Etching

6 jigs (racks) per tank × 2 tanks = 12 jigs
Treatment time: 3-15 minutes

Neutralization

6 jigs (racks) per tank × 1 tank = 6 jigs
Treatment time: 1-5 minutes

Anodizing

2 jigs (racks) per tank × 3 tanks = 6 jigs
Current density: 130A/m²
Process time: 30 minutes
Unprocess time: 10 minutes
Total time: 40 minutes

Average anodizing layer: 10-15µm

Colouring

Colour process: Mix Salts
2 jigs (racks) per tank × 1 tank = 2 jigs
Current density: 70A
Process time: 2-8 minutes

Sealing

Sealing method: Sealing at Medium or Normal Temperature
6 jigs (racks) per tank × 1 tank
Process time: 10-15 minutes

Design Parameters and Settings

Anodizing Treatment Area

Each anodizing process tank requires 40 minutes
Total jigs per year: (2 racks × 3 tanks × 60 min/h) ÷ 40 min × 600 hours = 5,400 jigs
Design: 57.1m² per jig (each tank: 114.2m²)
Area treatment per year: 5,400 jigs × 57.1m²/jig = 308,340m²

Anodizing Treatment Weight

Monthly output: 308,340m² ÷ 350m²/T × 0.9 = 792T ≥ 750T

Power Consumption

Anodising Tank: 100m²/tank × 130A/m² ÷ 0.9 = 14,444A per tank
Power Rectifier: 15,000A = 3 units
Colouring Tank: 100m²/tank × 70A/m² ÷ 0.9 = 7,777A per tank
Colour Rectifier: 8,000A = 1 unit

Process Chart Legend

Etiketler:

Eloksal Üretim Hattı

Otomatik Eloksal Hattı

Eloksal Hattı Ekipmanları

Eloksal Hattı Aksesuarları

Eloksal Atıksu Arıtma

Elektroforez Üretim Hattı

Alüminyum Ekstrüzyon Presi

toz kaplama hattı

Alüminyum Ekstrüzyon Taşıma Sistemi

Döküm Üretim Hattı

Alüminyum Profil Sarma Makinası

Eloksal Üretim Hattı

Otomatik Eloksal Hattı

Eloksal Hattı Ekipmanları

Eloksal Hattı Aksesuarları

Eloksal Atıksu Arıtma

Elektroforez Üretim Hattı

Alüminyum Ekstrüzyon Presi

toz kaplama hattı

Alüminyum Ekstrüzyon Taşıma Sistemi

Döküm Üretim Hattı

Alüminyum Profil Sarma Makinası

Ürün ayrıntıları

Eloksal Üretim Hattı

Otomatik Eloksal Hattı

Eloksal Hattı Ekipmanları

Eloksal Hattı Aksesuarları

Eloksal Atıksu Arıtma

Elektroforez Üretim Hattı

Alüminyum Ekstrüzyon Presi

toz kaplama hattı

Alüminyum Ekstrüzyon Taşıma Sistemi

Döküm Üretim Hattı

Alüminyum Profil Sarma Makinası

Intelligent Anodizing Line with 750T/month Output, 6500mm Max Profile Length, and 8-12µm Film Thickness

Eloksal Üretim Hattı

Yatay Eloksal Hattı

Alüminyum Eloksal Hattı